Nonaqueous electrolyte secondary battery and method for production of nonaqueous electrolyte secondary battery

ABSTRACT

Provided is a nonaqueous electrolyte secondary battery including a positive electrode, a negative electrode and a nonaqueous electrolyte, wherein the positive electrode has a positive active material containing a lithium transition metal composite oxide having an α-NaFeO 2 -type crystal structure and represented by the composition formula: Li 1+α Me 1−α O 2  (wherein Me is a transition metal element including Co, Ni and Mn; and α&gt;0), and the negative electrode has a negative active material which contains a carbon material that is a mixture of graphite and amorphous carbon and in which the ratio of the amorphous carbon contained in the carbon material is 5 to 60% by mass.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is based on Japanese Application No. 2012-150486 filedwith the Japan Patent Office on July 4 and Japanese Application No.2013-053061 filed with the Japan Patent Office on Mar. 15, 2013, theentire contents of which are hereby incorporated by reference.

FIELD

The present invention relates to a nonaqueous electrolyte secondarybattery and a method for production of the nonaqueous electrolytesecondary battery

BACKGROUND

Currently, nonaqueous electrolyte secondary batteries represented bylithium secondary batteries are widely mounted on portable devices, andso on. For these nonaqueous electrolyte secondary batteries, principallyLiCoO₂ is used as a positive active material. However, the dischargecapacity of LiCoO₂ is about 120 to 130 mAh/g.

As a material of a positive active material for a lithium secondarybattery, a solid solution of LiCoO₂ and other compounds is known.Li[Co_(1-2x)Ni_(x)Mn_(x)]O₂ (0<x≦½), a solid solution having anα-NaFeO₂-type crystal structure and formed of three components: LiCoO₂,LiNiO₂ and LiMnO₂, was published in 2001. LiNi_(1/2)Mn_(1/2)O₂ orLiCo_(1/3)Ni_(1/3)Mn_(1/3)O₂ that is one example of the aforementionedsolid solution has a discharge capacity of 150 to 180 mAh/g, and is alsoexcellent in terms of charge-discharge cycle performance.

In contrast with so-called a “LiMeO₂-type” positive active material asdescribed above, so-called a “lithium-excess-type” positive activematerial is known in which the composition ratio Li/Me of lithium (Li)to the ratio of a transition metal (Me) is greater than 1, with Li/Mebeing, for example, 1.25 to 1.6 (see, for example, U.S. Pat. No.6,677,082, U.S. Pat. No. 7,135,252, Japanese Patent No. 4877660 andJP-A-2010-50079). Such a material can be denoted as Li_(1+α)Me_(1−α)O₂(α>0). Here, β=(1+a)/(1−α) when the composition ratio Li/Me of lithium(Li) to the ratio of a transition metal (Me) is β, and therefore, forexample, α=0.2 when Li/Me is 1.5.

U.S. Pat. No. 6,677,082 and U.S. Pat. No. 7,135,252 describe a positiveactive material for a lithium secondary battery, which has the generalformula of xLiMO₂.(1−x)Li₂M′O₃ (0<x<1), The documents also describe thatM is at least one or more selected from Mn, Co and Ni and that M′ is Mn.The documents show that the positive active material enriched in Li hasa stabilized crystal structure, and a lithium secondary battery having ahigh discharge capacity is obtained by using this active material.

Japanese Patent No. 4877660 describes the invention of “an activematerial for a lithium secondary battery comprising a solid solution ofa lithium transition metal composite oxide having an α-NaFeO₂-typecrystal structure, wherein the composition ratio of Li, Co, Ni and Mncontained in the solid solution satisfiesLi_(1+(1/3)x)Co_(1−x−y)Ni_((1/2)y)Mn_((2/3)x+(1/2)y) (x+y≦1, 0≦y,1−x−y=z), (x, y, z) is represented by a value present on the line of orwithin a heptagon ABCDEFG having point A (0.45, 0.55, 0), point B (0.63,0.37, 0), point C (0.7, 0.25, 0.05), point D (0.67, 0.18, 0.15), point E(0.75, 0, 0.25), point F (0.55, 0, 0.45) and point G (0.45, 0.2, 0.35)as apexes, in aLi[Li_(1/3)Mn_(2/3)]O₂(x)-LiNi_(1/2)Mn_(1/2)O₂(y)-LiCoO₂(z)-systemtriangular phase diagram, and the intensity ratio of the diffractionpeak of the (003) line and the (104) line in X-ray diffractionmeasurement is I₍₀₀₃₎/I₍₁₀₄₎≧1.56 before charge-discharge, andI₍₀₀₃₎/I₍₁₀₄₎>1 at the end of discharge”, (claim 1), and shows that byusing the positive active material enriched in Li, a lithium secondarybattery, which has a high discharge capacity, and particularly has ahigh discharge capacity in a potential range of 4.3 V or less, isobtained.

On the other hand, a lithium secondary battery, wherein a positiveactive material containing a lithium transition metal composite oxideand a negative active material containing graphite and amorphous carbon(noncrystalline carbon) are combined, is well known (see, for example,JP-A-2010-50079, JP-A-2011-54371, JP-A-2012-15051 and JP-A-2012-84322).

JP-A-2010-50079 describes the invention of “a nonaqueous electrolytesecondary battery comprising: a positive electrode containing a positiveactive material; a negative electrode containing a negative activematerial; and a nonaqueous electrolyte having lithium ion conductivity,wherein the positive active material is a lithium-containing transitionmetal composite oxide having a layered structure and represented by thegeneral formula: Li_(1+x)(Ni_(a)Mn_(b)Co_(c))O_(2+a) (x+a+b+c=1,0.7≦a+b, 0<x≦0.1, 0≦c/(a+b)<0.35, 0.7≦a/b≦2.0, −0.1≦α≦0.1), and thenonaqueous electrolyte contains a lithium salt having an oxalate complexas an anion” (claim 1), and an object of the invention is to provide “anonaqueous electrolyte secondary battery using as a positive activematerial a lithium-containing transition metal oxide, which has alayered structure and in which the main component of the transitionmetal includes two elements: nickel and manganese, wherein thenonaqueous electrolyte secondary battery is excellent in powercharacteristics and low in cost” (paragraph [0010]).

JP-A-2010-50079 also describes that for the negative active material, “anoncrystalline carbon-coated graphite formed by coating a graphitematerial with noncrystalline carbon is suitably used from the viewpointof output/input characteristics” (paragraph [0033]); and a nonaqueouselectrolyte secondary battery, wherein a positive active material is“Li_(1.07)Ni_(0.42)Co_(0.09)Mn_(0.42)O₂” and a negative active materialis “a graphite coated on the surface with noncrystalline carbon”, asExample 8 (paragraphs [0042] and [0056] to [0058]”.

JP-A-2011-54371 describes the invention of “a lithium ion secondarybattery comprising: a positive electrode containing a positive activematerial capable of inserting/extracting lithium ions; a negativeelectrode containing, as a negative active material capable ofinserting/extracting lithium ions, a carbon material in which annoncrystalline carbon material constituting 55% by weight to 85% byweight (inclusive) of the whole negative active material and a graphitematerial constituting 15% by weight to 45% by weight (inclusive) of thewhole negative active material are mixed; and a nonaqueous electrolytesolution for wetting the positive electrode and negative electrode”(claim 1), and the invention “has as an object the provision of alithium ion secondary battery, of which input/output characteristics canbe improved” (paragraph [0007]).

JP-A-2011-54371 also describes that “by including as a negative activematerial a carbon material in which an noncrystalline carbon material asa principal material and a graphite material as an auxiliary materialare mixed, input characteristics can be improved because thenoncrystalline carbon material has a high charge capacity and highretention as compared to the graphite material, and powercharacteristics can be improved because the graphite material can keepthe battery voltage high and has a small reduction in power in an endstage of discharge as compared to the noncrystalline carbon material”(paragraph [0009]), and “for the positive active material, alithium-nickel-manganese-cobalt composite oxide is used; namely, it is acomposite oxide represented by the general formula:Li_(x)Ni_(y)Mn_(z)Co_((1−y−z−w))A_(w)O₂ and having a layered crystalstructure; here, in the general formula, x satisfies 0<x<1.2, and y andz satisfy y+z<1” (paragraph [0020]).

JP-A-2012-15051 describes the invention of “a negative electrode for alithium ion secondary battery, which comprises: a negative currentcollector; and a negative composite layer disposed on the negativecurrent collector and containing crystalline carbon and noncrystallinecarbon as a negative active material, wherein the negative compositelayer includes a plurality of layers, a layer closer to the negativecurrent collector has a higher content of crystalline carbon, a layerfarther from the negative current collector has a higher content ofnoncrystalline carbon, and in the layer closest to the negative currentcollector, the content of crystalline carbon is higher than the contentof noncrystalline carbon” (claim 1), “a lithium ion secondary batterycomprising: the negative electrode for a lithium ion secondary batteryaccording to any one of claims 1 to 6; and a positive electrodeincluding a positive current collector, and a positive composite layercontaining a positive active material” (claim 7), and “the lithium ionsecondary battery according to claim 7, wherein the positive activematerial is a lithium layered composite oxide represented by the generalformula: Li_(x)Ni_(y)Mn_(z)Co_((1−y−z−w))A_(w)O₂ [wherein 1.0≦x≦1.2,y+z+w<1, y≧z, 0≦w≦0.01, and A is at least one selected from the groupconsisting of Li, Al, Cr, Mg, Ti, B, F and W” (claim 8). JP-A-2012-15051also describes that “a lithium ion secondary battery using only agraphite carbon material as a negative active material has a problem interms of cycle life characteristics because input/output characteristicsare poor, and therefore degradation of the surface is significant inrepetition of high-rate charge-discharge although a high capacity isachieved; further, in . . . , the mixing ratio of graphite is low, andinput/output characteristics can be kept high, but it is difficult toachieve further capacity enhancement; therefore, capacity enhancementand improvement of cycle life characteristics of the lithium ionsecondary battery are desired” (paragraph [0008]), and “the weight ratioof crystalline carbon and noncrystalline carbon contained in thenegative composite layer is not particularly limited, but the amount ofcrystalline carbon contained in the whole layer is preferably largerthan the amount of noncrystalline carbon; specifically, the weight ratioof crystalline carbon and noncrystalline carbon is preferably 1.3:1 to10:1, especially preferably 1.5:1 to 5:1” (paragraph [0029]).

JP-A-2012-84322 describes a method for production of a lithium ionsecondary battery, comprising an assembly step of preparing a batterywhich contains in a battery case an electrode body having a positiveactive material and a negative active material, and an electrolytesolution containing a difluorophosphoric acid salt, wherein “thepositive active material is Li_(x)MO₂ (wherein M is Ni, or contains atleast any one of Al, Ti, V, Cr, Mn, Fe, Co, Cu, Zn, Mg, Ga, Zr and Si inaddition to Ni as a principal component), and satisfies 1.04≧X≦1.15”,and “particles of the negative active material include graphite andnoncrystalline carbon, and the ratio of the noncrystalline carbon in theparticles of the negative active material ranges from 2.5 to 7.1 wt %”(claim 1).

So-called a “lithium-excess-type” positive active material describedabove generally has a discharge capacity higher than that of so-called a“LiMeO₂-type” positive active material, and thus has such a feature thatby going through high-potential charge (high-potential formation) of 4.5V (vs. Li/Li⁺) or more in an initial charge-discharge step, a highdischarge capacity is achieved even if the charge potential issubsequently decreased.

SUMMARY

The following presents a simplified summary of the invention disclosedherein in order to provide a basic understanding of some aspects of theinvention. This summary is not an extensive overview of the invention.It is intended to neither identify key or critical elements of theinvention nor delineate the scope of the invention. Its sole purpose isto present some concepts of the invention in a simplified form as aprelude to the more detailed description that is presented later.

When the “lithium-excess-type” positive active material is combined witha negative electrode using graphite to prepare a nonaqueous electrolytesecondary battery with a positive-negative electrode capacity balancecomparable to that when a commercially available “LiMeO₂-type” positiveactive material is used, deposition of Li on the graphite negativeelectrode occurs during high-potential formation, and therefore cycleperformance is deteriorated. Thus, a nonaqueous electrolyte secondarybattery with such a positive-negative electrode capacity balance thatdeposition of Li does not occur is intended, but the problem in turnarises that the benefit of capacity enhancement by a“lithium-excess-type” positive active material cannot be obtained.Further, when a “lithium-excess-type” positive active material iscombined with a graphite negative electrode, the problem also arisesthat power performance in a low SOC (state of charge) region is low.

On the other hand, when amorphous carbon is used for a negativeelectrode, charge can be performed to a deeper utilization factor of thenegative electrode, and therefore an effect of suppressing deposition ofLi during initial high-potential formation is obtained, but there is theproblem that the actual capacity of a nonaqueous electrolyte secondarybattery is considerably reduced because the irreversible capacity duringinitial charge-discharge is large.

The present invention has been devised in view of the problems describedabove, and an object thereof is to provide a nonaqueous electrolytesecondary battery having a high battery capacity and a high power whilesuppressing deposition of Li on a negative electrode in high-potentialformation, and a method for production of the nonaqueous electrolytesecondary battery.

An aspect of the present invention includes a nonaqueous electrolytesecondary battery including a positive electrode, a negative electrodeand a nonaqueous electrolyte, wherein the positive electrode has apositive active material containing a lithium transition metal compositeoxide having an α-NaFeO₂-type crystal structure and represented by thecomposition formula: Li_(1+α)Me_(1−α)O₂ (wherein Me is a transitionmetal element including Co, Ni and Mn; and α>0). The negative electrodehas a negative active material containing a carbon material that is amixture of graphite and amorphous carbon, and the ratio of the amorphouscarbon contained in the carbon material is 5 to 60% by mass.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other features of the invention will become apparentto one skilled in the art to which the present invention relates uponconsideration of the invention with reference to the accompanyingdrawings, wherein:

FIG. 1 is a view showing a potential behavior during initialcharge-discharge step performed during a production process of anonaqueous electrolyte secondary battery for a positive electrode havinga positive active material prepared in Example 1-1;

FIG. 2 is a view showing a potential behavior of a negative electrodehaving a negative active material containing a mixture of graphite andamorphous carbon; and

FIG. 3 is a view showing a potential behavior of a negative electrodehaving a negative active material composed of graphite.

DESCRIPTION OF EMBODIMENTS

A nonaqueous electrolyte secondary battery including a positiveelectrode, a negative electrode and a nonaqueous electrolyte, whereinthe positive electrode has a positive active material containing alithium transition metal composite oxide having an α-NaFeO₂-type crystalstructure and represented by the composition formula: Li_(1+α)Me_(1−α)O₂(wherein Me is a transition metal element including Co, Ni and Mn; andα>0). The negative electrode has a negative active material containing acarbon material that is a mixture of graphite and amorphous carbon, andthe ratio of the amorphous carbon contained in the carbon material is 5to 60% by mass.

Another aspect of this nonaqueous electrolyte secondary battery has theamorphous carbon having a half width of 6.0° or less, the half widthbeing that of the (002) diffraction line in X-ray diffractionmeasurement.

In another aspect, the positive active material using this nonaqueouselectrolyte secondary battery contains Na.

A method for production of the nonaqueous electrolyte secondary batteryaccording to the present invention includes a charge step which at leastleads to a region where a potential change occurring, with respect to acharging electric quantity, in a positive electrode potential range ofmore than 4.3 V (vs. Li/Li⁺) and 4.8 V (vs. Li/Li⁺) or less isrelatively flat.

A charge step for production of the nonaqueous electrolyte secondarybattery according to the present invention is a charge step in aninitial charge-discharge step.

A method for production of a nonaqueous electrolyte secondary batteryaccording to the present invention includes a charge step in which acharge capacity per negative active material is 372 mAh/g or more in thecharge step.

According to the present invention, a nonaqueous electrolyte secondarybattery is obtained which has a high battery capacity and a high powerwhile deposition of Li on a negative electrode during high-potentialformation is suppressed. The half width of amorphous carbon, which ismixed with graphite as a negative active material, is kept at a specificvalue or less to increase discharge energy of the nonaqueous electrolytesecondary battery.

The composition of a lithium transition metal composite oxide containedin an active material for a lithium secondary battery according to thepresent invention can be denoted as Li_(1+α)Me_(1−α)O₂ (α>0) whichcontains a transition metal element Me including Co, Ni and Mn as wellas Li. The lithium transition metal composite oxide is so called a“lithium-excess type” which has a high discharge capacity.

The ratio of elements such as Co, Ni and Mn which form a transitionmetal element that forms the lithium transition metal composite oxidecan be arbitrarily selected according to required characteristics.

In the present invention, the molar ratio of Li to the transition metalelement Me (Li/Me), which is represented by (1+α)/(1−α) in thecomposition formula of Li_(1+α)Me_(1−α)O₂, is preferably 1.2 to 1.6because a lithium secondary battery having a high discharge capacity canbe obtained. Above all, a composition in which the ratio of Li/Me is1.25 to 1.45 is more preferably selected to obtain a lithium secondarybattery which has a particularly high discharge capacity and isexcellent in high rate discharge characteristics.

The molar ratio of Co to the transition metal element Me (Co/Me) ispreferably 0.02 to 0.23, more preferably 0.04 to 0.21, most preferably0.06 to 0.17, to obtain a lithium secondary battery which has a highdischarge capacity and is excellent in initial charge-dischargeefficiency.

The molar ratio of Mn to the transition metal element Me (Mn/Me) ispreferably 0.63 to 0.72, more preferably 0.65 to 0.71, to obtain alithium secondary battery which has a high discharge capacity and isexcellent in initial charge-discharge efficiency.

In the present invention, the lithium transition metal composite oxiderepresented by the composition formula of Li_(1+α)Me_(1−α)O₂ (Me is atransition metal including Co, Ni and Mn and α>0) is preferably tocontain Na in an amount of 900 ppm or more.

Improvement of the discharge capacity is not sufficient if the contentof Na is less than 900 ppm, while the discharge capacity starts todecrease, applying paste stability is deteriorated, and processabilityin preparation of the electrode is deteriorated if the content of Na ismore than 16000 ppm. Therefore, for improving the discharge capacity,the content of Na is set to be no less than 900 ppm and no more than16000 ppm. The content of Na is preferably 1000 ppm or more and 12000ppm or less, more preferably 2000 ppm or more and 10000 ppm or less.

For adjusting the content of Na to the range described above, a methodin which in a step of preparing a carbonate precursor as describedlater, a sodium compound such as sodium carbonate is used as aneutralizer, so that Na remains in a washing step, and/or a method inwhich in a subsequent sintering step, a sodium compound such as sodiumcarbonate is added can be employed.

In a step of preparing a carbonate precursor, when a sodium compoundsuch as sodium carbonate is used as a neutralizer, the carbonateprecursor is able to contain Na in an amount of 900 ppm or more and lessthan 2100 ppm.

Residual Na in the neutralization/washing step during preparation of theprecursor may act as a primary particle growth suppressing agent in astep of sintering so called a “lithium-excess-type” lithium transitionmetal composite oxide, and the electrode characteristic of a lithiumsecondary battery including the lithium transition metal composite oxideas a positive active material may be improved.

The lithium transition metal composite oxide of the present invention isrepresented by the general formula described above, is a composite oxideessentially composed of Li, Co, Ni and Mn, and contains a small amountof Na, but inclusion of a small amount of other metals, alkali metalssuch as K, alkali earth metals such as Mg and Ca and transition metalsrepresented by 3d transition metals such as Fe and Zn within the boundsof not impairing the effect of the present invention, is not excluded.

The lithium transition metal composite oxide according to the presentinvention has an α-NaFeO₂ structure. The lithium transition metalcomposite oxide after synthesis (before charge-discharge is performed)is attributed to the space group P3₁12 or R3−m. Among them, in thoseattributed to the space group P3₁12, a superlattice peak (peak found ina (Li[Li_(1/3)Mn_(2/3)]O₂-type monoclinic crystal) is observed at around2θ=21° on an X-ray diffraction pattern using a CuKα radiation. However,when charge is carried out at least once, so that Li in the crystal isdeintercalated, the symmetry of the crystal is changed, and consequentlythe superlattice peak disappears, and the lithium transition metalcomposite oxide is attributed to the space group R3−m. Here, P3₁12 is acrystal structure model in which atom positions at 3a, 3b and 6c sitesin R3−m are subdivided, and the P3₁12 model is employed when there isorderliness in atom arrangement in R3−m. Properly speaking, “R3−m”should be written with a bar “−” added above “3” of “R3m”.

The lithium transition metal composite oxide according to the presentinvention is attributed to the space group P3₁12 or R3−m of thehexagonal crystal, and preferably the half width of the diffraction peakat 2θ=18.6°±1° is 0.20° to 0.27° or/and the half width of thediffraction peak at 2θ=44.1°±1° is 0.26° to 0.39° on an X-raydiffraction pattern using a CuKα radiation. In this way, the dischargecapacity of the positive active material can be increased. Thediffraction peak at 2θ=18.6°±1° is indexed to the (003) line in themirror index hkl for space groups P3₁12 and R3−m, and the diffractionpeak at 2θ=44.1°±1° is indexed to the (114) line for the space groupP3₁12 and to the (104) line for the space group R3−m, respectively.

In another aspect of the present invention, the positive active materialfor a lithium secondary battery and the carbonate precursor thereof arepreferably to have a 50% particle size (D50) of 5 to 10 μm in particlesize distribution measurement. When the lithium transition metalcomposite oxide is prepared from a hydroxide precursor, excellentperformance is not achieved unless the particle size is controlled to besmaller. By preparing the lithium transition metal composite oxide froma carbonate precursor, an active material having large dischargecapacity is obtained even when the 50% particle size (D50) in particlesize distribution measurement is 5 to 10 μm.

An active material prepared by way of a carbonate precursor has a peakdifferential pore volume of 0.85 mm³/(g·nm) or more in a pore region of30 to 50 nm, whereas an active material prepared by way of a hydroxideprecursor has a peak differential pore volume of only about 0.50mm³/(g·nm) in a pore region of 30 to 50 nm, and the differential peak isin a pore region of about 60 nm.

In the lithium transition metal composite oxide according to anotheraspect of the present invention, the pore size, at which thedifferential pore volume determined by a BJH method from an adsorptionisotherm obtained using a nitrogen gas adsorption method shows a maximumvalue, is in a range of 30 to 40 nm, and the peak differential porevolume is 0.85 mm³/(g·nm) or more. Since the peak differential porevolume is 0.85 mm³/(g·nm) or more, a lithium secondary battery excellentin initial efficiency can be obtained. When the peak differential porevolume is 1.76 mm³/(g·nm) or less, a lithium secondary battery, which isnot only excellent in initial efficiency but also particularly excellentin discharge capacity, can be obtained, and therefore the peakdifferential pore volume is preferably 0.85 to 1.76 mm³/(g·nm).

Next, a method for producing the active material for a non-aqueouselectrolyte lithium secondary battery according to the present inventionwill be described.

The active material for a non-aqueous electrolyte lithium secondarybattery of the present invention can be obtained basically by preparinga raw material which contains, in accordance with the composition of anintended active material (oxide), metal elements (Li, Mn, Co, Ni and Na)that forms the active material, and sintering the raw material.

For preparing an oxide having an intended composition, so called a“solid state method” in which salts of Li, Co, Ni, Mn and Na,respectively, are mixed and sintered, and a “coprecipitation method” inwhich a coprecipitation precursor with Co, Ni and Mn existing in oneparticle is prepared beforehand, a Li salt and a Na salt are mixed andsintered therewith are known. In a synthesis process by the “solid statemethod”, it is difficult to obtain a sample with the elementshomogeneously distributed in one particle because Mn in particular ishard to be homogeneously solid soluted in Co and Ni. In literatures andthe like, a large number of attempts to solid-dissolve Mn in a part ofNi and Co by the solid phase method have been hitherto made(LiNi_(1−x)Mn_(x)O₂, etc.), but a homogeneous phase is more easilyobtained at an element level by selection of the “coprecipitationmethod”. Thus, in Examples described later, the “coprecipitation method”is employed.

For preparing a coprecipitation precursor, it is very important toestablish an inert atmosphere in a solution from which thecoprecipitation precursor is to be obtained. Among Co, Ni and Mn, Mn iseasily oxidized, so that it is not easy to prepare a coprecipitationhydroxide with Co, Ni and Mn homogeneously distributed in a divalentstate, and therefore homogeneous mixing of Co, Ni and Mn at an elementlevel tends to be incomplete. Particularly in the composition range inthe present invention, the ratio of Mn is high as compared to the ratiosof Co and Ni, and therefore it is particularly important to removedissolved oxygen in an aqueous solution. Examples of the method forremoving dissolved oxygen include a method in which a gas containing nooxygen is bubbled. The gas containing no oxygen is not limited, but anitrogen gas, an argon gas, carbon dioxide (CO₂) or the like can beused.

Particularly, when a coprecipitation carbonate precursor is prepared asin Example described later, employment of carbon dioxide as a gascontaining no oxygen is preferable because an environment is provided inwhich the carbonate is more easily generated.

A pH in the step of producing a precursor by coprecipitating in asolution a compound containing Co, Ni and Mn is not limited, but can beset at 7.5 to 11 when the coprecipitation precursor is prepared as acoprecipitation carbonate precursor. It is preferable to control pH forincreasing the tap density. By setting pH at 9.4 or less, it can beensured that the tap density is 1.25 g/cm³ or more, so that high-ratedischarge performance can be improved. Further, by setting pH at 8.0 orless, the particle growth rate can be accelerated, so that the stirringduration after completion of dropwise addition of a raw material aqueoussolution can be reduced.

The coprecipitation precursor core is preferably a compound with Mn, Niand Co mixed homogeneously. In the present invention, thecoprecipitation precursor is preferably a carbonate for obtaining anactive material for a lithium secondary battery, which has a highdischarge capacity. A precursor having a higher bulk density can also beprepared by using a crystallization reaction using a complexing agent.At this time, by carrying out mixing/sintering with a Li source, anactive material having a high density, so that the energy density perelectrode area can be increased.

Examples of the raw material of the coprecipitation hydroxide precursormay include manganese oxide, manganese carbonate, manganese sulfate,manganese nitrate and manganese acetate as a Mn compound, nickelhydroxide, nickel carbonate, nickel sulfate and nickel acetate as a Nicompound, and cobalt sulfate, cobalt nitrate and cobalt acetate as a Cocompound.

In the present invention, a reaction crystallization method forobtaining a coprecipitation carbonate precursor by adding dropwise a rawmaterial aqueous solution of the coprecipitation precursor into areaction tank kept alkaline is employed. A sodium compound such assodium carbonate is used as a neutralizer, but it is preferred to usesodium carbonate or a mixture of sodium carbonate and lithium carbonate.Na/Li, which is a molar ratio of sodium carbonate to lithium carbonate,is preferably 0.85/1.15 [M] or more for ensuring that Na remains in anamount of 900 ppm or more as shown in Example described later. Bysetting Na/Li at 0.85/1.15 [M] or more, the possibility can be reducedthat Na is excessively removed in a subsequent washing step, so that thecontent of Na is less than 900 ppm.

The rate of dropwise addition of the raw material aqueous solutionsignificantly influences homogeneity of the element distribution withinone particle of the coprecipitation precursor generated. Particularly,Mn is hard to form a homogeneous element distribution with Co and Ni,and therefore requires care. For the preferred dropwise addition rate,it depends on the size of the reaction tank, stirring conditions, pH,the reaction temperature and so on, but is preferably 30 ml/min or less.For increasing the discharge capacity, the dropwise addition rate ismore preferably 10 ml/min or less, most preferably 5 ml/min or less.

When a complexing agent is present in the reaction tank, and certainconvection conditions are applied, rotation and revolution of particlesin a stirring tank are promoted by further continuing stirring aftercompletion of dropwise addition of the raw material aqueous solution,and in this process, particles are grown stepwise into a concentriccircular sphere while colliding with one another. That is,coprecipitation precursor is formed through reactions in two stages,i.e. a metal complex formation reaction when the raw material aqueoussolution is added dropwise into the reaction tank and a precipitateformation reaction that occurs during retention of the metal complex inthe reaction tank. Therefore, by appropriately selecting a time duringwhich stirring is further continued after completion of dropwiseaddition of the raw material aqueous solution, a coprecipitationprecursor having a desired particle size can be obtained.

For the preferred stirring duration time after completion of dropwiseaddition of the raw material aqueous solution, it depends on the size ofthe reaction tank, stirring conditions, pH, the reaction temperature andso on, but is, for example, preferably 0.5 h or more, more preferably 1h or more for growing particles as uniform spherical particles. Forreducing the possibility that the particle size is so large that thepower performance of the battery in the low SOC region is notsufficient, the time is preferably 15 h or less, more preferably 10 h orless, most preferably 5 h or less.

The preferred stirring duration time for ensuring that D50, i.e. aparticle size is 5 to 10 μm, at which the cumulative volume in theparticle size distribution of secondary particles of the carbonateprecursor and the lithium transition metal composite oxide is 50%,varies depending on controlled pH. For example, the stirring durationtime is preferably 3 to 7 h when pH is controlled to 8.3 to 8.9, and thestirring duration time is preferably 1 to 5 h when pH is controlled to7.5 to 8.0.

When particles of the carbonate precursor are prepared using as aneutralizer a sodium compound such as sodium carbonate, sodium ionsdeposited on particles are washed off in a subsequent washing step, andin the present invention, it is preferably to wash off sodium ions undersuch conditions that Na remains in an amount of 900 ppm or more. Forexample, such conditions that the number of washings with 200 ml ofion-exchange water is 5 can be employed when the prepared carbonateprecursor is extracted by suction filtration.

Preferably the carbonate precursor is dried under normal pressure in anair atmosphere at a temperature of 80° C. to lower than 100° C. A largeramount of moisture can be removed in a short time when the carbonateprecursor is dried at 100° C. or higher, but an active material showingmore excellent electrode characteristics can be formed when thecarbonate precursor is dried at 80° C. for a long time. Although thereason for this is not necessarily evident, the carbonate precursor is aporous material having a specific surface area of 50 to 100 m²/g, andtherefore has a structure in which moisture is easily adsorbed. Thus,the inventor presumes as follows: When the carbonate precursor is driedat a low temperature to ensure that measurable adsorbed water remains ina pore in the state of the precursor. Molten Li can enter the pore insuch a manner as to replace adsorbed water that is removed from the porein a sintering step of mixing the carbonate precursor with a Li salt andsintering the mixture. Consequently an active material having a moreuniform composition is obtained as compared to the case where thecarbonate precursor is dried at 100° C. Since a carbonate precursorobtained by performing drying at 100° C. shows is deep brown, while acarbonate precursor obtained by performing drying at 80° C. isfresh-colored, a distinction can be made by the color of the precursor.

Thus, for quantitatively evaluating the above-described differencebetween the precursors, the color phase of each precursor was measuredand compared with JPMA Standard Paint Colors (Edition F, 2011) beingcompliant with JIS Z 8721 and issued by Japan Paint ManufacturersAssociation. For measurement of the color phase, Color Leader CR10manufactured by KONICA MINOLTA, INC was used. According to thismeasurement method, the value of dL* that represents a brightness islarger when the sample is more whitish, and is smaller when the sampleis more blackish. The value of da* that represents a color phase islarger when the sample is more reddish, and is smaller when the sampleis more greenish (less reddish). The value of db* that represents acolor phase is larger when the sample is more yellowish, and is smallerwhen the sample is more bluish (less yellowish).

It has become apparent that the color phase of a product by drying at100° C. (Comparative Example) is within a range in which the standardcolor F05-40D is attained in a red direction as compared to the standardcolor F05-20B, and is within a range in which the standard color FN-25is attained in a white direction as compared to the standard colorFN-10. It has been found that above all, a color difference between theabove-mentioned color phase and a color phase exhibited by the standardcolor F05-20B is smallest.

It has become apparent that the color phase of a product by drying at80° C. (Example) is within a range in which the standard color F19-70Fis attained in a white direction as compared to the standard colorF19-50F, and is within a range in which the standard color F09-60H isattained in a black direction as compared to the standard color F09-80D.It has been found that above all, a color difference between theabove-mentioned color phase and a color phase exhibited by the standardcolor F19-50F is smallest.

From the above findings, it can be said that preferably the color phaseof the carbonate precursor is in the +direction in all of dL, da and dbas compared to the standard color F05-20B, and more preferably dL is +5or more, da is +2 or more, and db is +5 or more.

By above-described the range of the color phase for precursor, thepositive active material has a larger discharge capacity. The positiveactive material for a nonaqueous electrolyte lithium secondary batteryaccording to the present invention can be suitably prepared by mixingthe carbonate precursor and a Li compound, followed by heat-treating themixture. By using, as the Li compound, lithium hydroxide, lithiumcarbonate, lithium nitrate, lithium acetate or the like, the activematerial can be suitably produced. For the amount of the Li compound,however, it is preferable to incorporate the Li compound in an excessiveamount by about 1 to 5% in consideration of elimination of a partthereof during sintering.

In the present invention, a Na compound is preferably mixed with thecarbonate precursor containing Na, together with a Li compound, in thesintering step for ensuring that the content of Na in the lithiumtransition metal composite oxide is 3000 ppm or more. The Na compound ispreferably sodium carbonate. The content of Na in the carbonateprecursor is about 900 to 2100 ppm, but the content of Na can beincreased to 3000 ppm or more by mixing a Na compound.

The sintering temperature influences the reversible capacity of theactive material.

If the sintering temperature is too high, there is such a tendency thatthe obtained active material is collapsed with an oxygen releasereaction, and a phase defined as a Li[Li_(1/3)Mn_(2/3)]O₂ type of amonoclinic crystal, in addition to a hexagonal crystal as a main phasetends to be observed as a separate phase rather than a solid solutionphase. Inclusion of this separate phase in a too large amount is notpreferable because the reversible capacity of the active material isreduced. In this material, impurity peaks are observed at around 35° andat around 45° on the X-ray diffraction pattern. Therefore, the sinteringtemperature is preferably lower than a temperature at which the oxygenrelease reaction of the active material is influential.

On the other hand, if the sintering temperature is too low, there issuch a tendency that crystallization does not sufficiently proceed, andthe electrode characteristic is degraded. In the present invention, thesintering temperature is preferably at least 700° C. By ensuringsufficient crystallization, the resistance of a crystal grain boundarycan be reduced to facilitate smooth transportation of lithium ions.

As described above, the preferred sintering temperature varies dependingon the oxygen release temperature of the active material, and it istherefore difficult to uniformly set a preferred range of the sinteringtemperature, but for making the discharge capacity sufficiently highwhen the molar ratio of Li/Me is 1.2 to 1.6, the sintering temperatureis preferably 700 to 950° C., and more preferably around 800 to 900° C.particularly when Li/Me is 1.25 to 1.4

In the present invention, a carbon material capable of absorbing andreleasing lithium ions is used as a negative active material. Here, thecarbon material is composed of a mixture of graphite and amorphouscarbon, and the ratio of the aforementioned amorphous carbon containedin the carbon material is 5 to 60% by mass.

Amorphous carbon is carbon satisfied at least one of “a crystalstructure which does not show an orientation only in a specificmonoaxial direction” or “a d₍₀₀₂₎ determined from the (002) diffractionline in X-ray diffraction measurement is 3.4 Å or more”. Specificexamples thereof include soft carbon and hard carbon.

In the present invention, use of amorphous carbon having a half width of6.0° or less, the half width being that of the (002) diffraction line inX-ray diffraction measurement, is preferable because discharge energy ofthe nonaqueous electrolyte secondary battery can be increased. Further,the half width is preferably 5.1° or less, especially preferably 3.2° orless.

A negative electrode composed of amorphous carbon has a low dischargecapacity as compared to a negative electrode composed of graphite, buthas a large effect of suppressing deposition of Li during charge.Therefore, by mixing amorphous carbon with graphite to form a negativeactive material, charge can be performed to a deeper utilization factorof the negative electrode in high-potential formation in an initialcharge-discharge step. That is, the discharge capacity of the negativeelectrode can be made larger by inserting into amorphous carbon anamount of Li⁺ which corresponds to a difference between a positiveelectrode capacity during high-potential formation and a positiveelectrode capacity during actual use.

By mixing amorphous carbon with graphite to form a negative activematerial, a low SOC region having a high resistance, which is a weakpoint of the “lithium-excess-type” positive active material, can be cut,leading to the advantage that the low SOC power is improved.

If the ratio of the amorphous carbon contained in the carbon material isless than 5% by mass (the ratio of graphite is more than 95%),deposition of Li occurs on a negative electrode having graphite as aprincipal component during high-potential formation in an initialcharge-discharge step, so that cycle performance is deteriorated, andthe low SOC power is not improved. If the ratio of the amorphous carboncontained in the carbon material is more than 60% by mass (the ratio ofgraphite is less than 40%), the battery capacity is reduced. Therefore,for increasing the battery capacity and improving the low SOC power, theratio of the amorphous carbon contained in the carbon material is 5 to60% by mass. For more increasing the battery capacity and improving thelow SOC power, the ratio of the amorphous carbon contained in the carbonmaterial is preferably 10 to 50% by mass, more preferably 10 to 30% bymass. Since initial efficiency is significantly improved as the ratio ofthe amorphous carbon is decreased from 60% by mass or less to 50% bymass or less, further to 30% by mass or less, the aforementioned rangeis preferable.

It is desirable that the powder of the positive active material and thepowder of the negative electrode material have an average particle sizeof 100 μm or less. Particularly, it is desirable that the powder of thepositive active material have a size of 10 μm or less for the purpose ofimproving the high power characteristics of the nonaqueous secondaryelectrolyte battery. A crusher and a classifier are used for obtaining apowder in a predetermined shape. For example, a mortar, a ball mill, asand mill, a vibration ball mill, a planet ball mill, a jet mill, acounter jet mill, a revolving airflow-type jet mill, a sieve or the likeis used. At the time of crushing, wet crushing can also be used in whichwater, or an organic solvent such as hexane coexists. The classificationmethod is not particularly limited, and a sieve, an air classifier orthe like is used as necessary in both dry and wet processes.

The positive active material and the negative electrode material whichare main components of the positive electrode and the negative electrodehave been described in detail above, but the positive electrode andnegative electrode may contain, in addition to the main components, aconducting agent, a binder, a thickener, a filler and the like as othercomponents.

The conducting agent is not limited as long as it is anelectron-conductive material that has no adverse effect on batteryperformance, but normally conductive materials such as natural graphite(scaly graphite, flake graphite, earthy graphite, etc.), artificialgraphite, carbon black, acetylene black, ketjen black, carbon whisker,carbon fibers, metal (copper, nickel, aluminum, silver, gold, etc.)powders, metal fibers and conductive ceramic materials can be includedalone or as a mixture thereof.

Among them, acetylene black is desirable as a conducting agent from theviewpoints of electron conductivity and coating properties. The addedamount of the conducting agent is preferably 0.1% by weight to 50% byweight, especially preferably 0.5% by weight to 30% by weight based onthe total weight of the positive electrode or negative electrode.Particularly, use of acetylene black crushed into ultrafine particles of0.1 to 0.5 μm is desirable because the required amount of carbon can bereduced. These mixing methods involve physical mixing, the ideal ofwhich is homogeneous mixing. Thus, mixing can be carried out in a dryprocess or a wet process using a powder mixer such as a V-type mixer, anS-type mixer, a grinder, a ball mill or a planet ball mill.

As the binder, thermoplastic resins such as polytetrafluoroethylene(PTFE), polyvinylidene fluoride (PVDF), polyethylene and polypropylene,and polymers having rubber elasticity, such as ethylene-propylene-dieneterpolymer (EPDM), sulfonated EPDM, styrene-butadiene rubber (SBR) andfluororubber can normally be used alone or as a mixture of two or morethereof. The added amount of the binder is preferably 1 to 50% byweight, especially preferably 2 to 30% by weight based on the totalweight of the positive electrode or negative electrode.

The filler may be any material as long as it has no adverse effect onbattery performance. An olefin-based polymer such as polypropylene orpolyethylene, amorphous silica, alumina, zeolite, glass, carbon or thelike is normally used. The added amount of the filler is preferably 30%by weight or less based on the total amount of the positive electrode orthe negative electrode.

The positive electrode and the negative electrode are suitably preparedby kneading the aforementioned main components (positive active materialin the positive electrode and negative electrode material in thenegative electrode) and other materials to form a mixture, and mixingthe mixture with an organic solvent, such as N-methylpyrrolidone ortoluene, or water, followed by applying or contact-bonding the resultingmixed liquid onto a current collector that is described in detail below,and carrying out a heating treatment at a temperature of about 50° C. to250° C. for about 2 hours. For the applying method, for example, it isdesirable to perform applying in any thickness and any shape using meanssuch as roller coating by an applicator roll or the like, screencoating, a doctor blade system, spin coating or a bar coater, but theapplying method is not limited thereto.

The nonaqueous electrolyte used in the nonaqueous electrolyte secondarybattery according to the present invention is not limited, and thosethat are generally proposed to be used in lithium batteries and the likecan be used. Examples of the nonaqueous solvent used in the nonaqueouselectrolyte may include, but are not limited to, cyclic carbonates suchas propylene carbonate, ethylene carbonate, butylene carbonate,chloroethylene carbonate and vinylene carbonate; cyclic esters such asγ-butyrolactone and γ-valerolactone; chain carbonates such as dimethylcarbonate, diethyl carbonate and ethylmethyl carbonate; chain esterssuch as methyl formate, methyl acetate and methyl butyrate;tetrahydrofuran or derivatives thereof; ethers such as 1,3-dioxane,1,4-dioxane, 1,2-dimethoxyethane, 1,4-dibutoxyethane and methyl diglyme;nitriles such as acetonitrile and benzonitrile; dioxolane or derivativesthereof; and ethylene sulfide, sulfolane, sultone or derivatives thereofalone or mixtures of two or more thereof.

Examples of the electrolyte salt used in the nonaqueous electrolyteinclude inorganic ion salts including one of lithium (Li), sodium (Na)and potassium (K), such as LiClO₄, LiBF₄, LiAsF₆, LiPF₆, LiSCN, LiBr,LiI, Li₂SO₄, Li₂B₁₀Cl₁₀, NaClO₄, NaI, NaSCN, NaBr, KClO₄ and KSCN, andorganic ion salts such as LiCF₃SO₃, LiN(CF₃SO₂)₂, LiN(C₂F₅SO₂)₂,LiN(CF₃SO₂)(C₄F₉SO₂), LiC(CF₃SO₂)₃, LiC(C₂F₅SO₂)₃, (CH₃)₄NBF₄,(CH₃)₄NBr, (C₂H₅)₄NClO₄, (C₂H₅)4NI, (C₃H₇)₄NBr, (n-C₄H₉)₄NClO₄,(n-C₄H₉)₄NI, (C₂H₅)₄N-maleate, (C₂H₅)₄N-benzoate, (C₂H)₄N-phtalate,lithium stearylsulfonate, lithium octylsulfonate and lithiumdodecylbenzenesulfonate, and these ionic compounds can be used alone orin combination of two or more thereof.

Further, by mixing LiPF₆ or LiBF₄ with a lithium salt having aperfluoroalkyl group, such as LiN (C₂F₅SO₂)₂, the viscosity of theelectrolyte can be further reduced, so that the low-temperaturecharacteristics can be further improved, and self discharge can besuppressed, thus being more desirable.

A salt that is melted at ordinary temperature or an ion liquid may beused as a nonaqueous electrolyte.

The concentration of the electrolyte salt in the nonaqueous electrolyteis preferably 0.1 mol/l to 5 mol/l, further preferably 0.5 mol/l to 2.5mol/l for reliably obtaining a nonaqueous electrolyte secondary batteryhaving high battery characteristics.

As a separator, it is preferable that a porous membrane, a nonwovenfabric or the like, which shows excellent high rate dischargeperformance, be used alone or in combination. Examples of the materialthat forms the separator for a nonaqueous electrolyte secondary batterymay include polyolefin-based resins represented by polyethylene,polypropylene and the like, polyester-based resins represented bypolyethylene terephthalate, polybutylene terephthalate and the like,polyvinylidene fluoride, vinylidene fluoride-hexafluoropropylenecopolymers, vinylidene fluoride-perfluoro vinyl ether copolymers,vinylidene fluoride-tetrafluoroethylene copolymers, vinylidenefluoride-trifluoroethylene copolymers, vinylidenefluoride-fluoroethylene copolymers, vinylidenefluoride-hexafluoroacetone copolymers, vinylidene fluoride-ethylenecopolymers, vinylidene fluoride-propylene copolymers, vinylidenefluoride-trifluoropropylene copolymers, vinylidenefluoride-tetrafluoroethylene-hexafluoropropylene copolymers andvinylidene fluoride-ethylene-tetrafluoroethylene copolymers.

The porosity of the separator is preferably 98% by volume or less fromthe viewpoint of the strength. The porosity is preferably 20% by volumeor more from the viewpoint of charge-discharge characteristics.

For the separator, for example, a polymer gel formed of acrylonitrile,ethylene oxide, propylene oxide, methyl methacrylate, vinyl acetate,vinyl pyrrolidone or a polymer such as poly(fluoride vinylidene) and anelectrolyte may be used. Use of the nonaqueous electrolyte in a gel formas described above is preferable from the viewpoint of being effectiveto prevent liquid leakage.

Further, for the separator, use of the porous membrane, nonwoven fabricor the like in combination with the polymer gel is desirable becauseliquid retainability of the electrolyte is improved. That is, a filmwith the surface and the microporous wall face of a polyethylenemicroporous membrane coated with a solvophilic polymer in a thickness ofseveral μm or less is formed, and an electrolyte is held withinmicropores of the film, so that the solvophilic polymer is formed into agel.

Examples of the solvophilic polymer include, in addition topoly(fluoride vinylidene), polymers in which an acrylate monomer havingan ethylene oxide group, an ester group or the like, an epoxy monomer, amonomer having an isocyanate group, or the like is crosslinked. Themonomer can be subjected to a crosslinking reaction by carrying outheating or using ultraviolet rays (UV) while using a radical initiatorat the same time, or using active light rays such as electron beams(EB), or the like.

The configuration of the nonaqueous electrolyte secondary batteryaccording to the present is not particularly limited, and examplesthereof include a cylindrical battery having a positive electrode, anegative electrode and a roll-shaped separator, a prismatic battery anda flat battery.

Both the conventional positive active material and the active materialusing the nonaqueous electrolyte secondary battery according to thepresent invention are capable of charge-discharge at a positiveelectrode potential of around 4.5 V (vs. Li/Li⁺). However, depending onthe type of using nonaqueous electrolyte, the nonaqueous electrolyte maybe oxidatively decomposed to cause deterioration of battery performancebecause the positive electrode potential during charge is too high. Anonaqueous electrolyte secondary battery, with which a sufficientdischarge capacity is obtained even when such a charge method that themaximum potential of the positive electrode during charge is 4.3 V (vs.Li/Li⁺) or less is employed at the time of operation, may be required.If the active material using the nonaqueous electrolyte secondarybattery of the present invention is used, a discharge electrical amount,which exceeds the capacity of the conventional positive active material,i.e., about 200 mAh/g, can be obtained even when such a charge methodthat the maximum potential of the positive electrode during charge islower than 4.5 V (vs. Li/Li⁺), for example, 4.4 (vs. Li/Li⁺) or less or4.3 (vs. Li/Li⁺) or less is employed at the time of user operation.

For the positive active material using the nonaqueous electrolytesecondary battery, according to the present invention to have a highdischarge capacity, the ratio, at which transition metal elements thatform a lithium-transition metal composite oxide are present in areasother than transition metal sites of a layered rock-salt-type crystalstructure, is preferably low. This can be achieved by ensuring that inprecursor particles that are subjected to a sintering step, transitionmetal elements such as Co, Ni and Mn in precursor core particles aresufficiently homogeneously distributed, and selecting suitableconditions for the sintering step for promoting crystallization of anactive material. If distribution of transition metals in precursor coreparticles that are subjected to the sintering step is not homogeneous, asufficient discharge capacity is not obtained. The reason for this isnot necessarily clear, but the present inventors infer that this resultsfrom occurrence of so called cation mixing in which the obtainedlithium-transition metal composite oxide has some of transition metalelements present in areas other than transition metal sites of thelayered rock-salt-type crystal structure, i.e., lithium sites if thedistribution of transition metals in precursor core particles that aresubjected to the sintering step is not homogeneous. A similar inferencecan be applied in a crystallization process in the sintering step,wherein cation mixing in the layered rock-salt-type crystal structureeasily occurs if crystallization of the active material is insufficient.Those in which the homogeneity of the distribution of the transitionmetal elements is high tend to have a high intensity ratio ofdiffraction peaks of the (003) line and the (104) line when the resultof X-ray diffraction measurement is attributed to a space group R3−m. Inthe present invention, the intensity ratio of diffraction peaks of the(003) line and the (104) line from X-ray diffraction measurement ispreferably I₍₀₀₃₎/I₍₁₀₄₎≧1.0. The intensity ratio is preferablyI₍₀₀₃₎/I₍₁₀₄₎>1 in a state of complete discharge after charge-discharge.If synthesis conditions and synthesis procedures for the precursor areinappropriate, the peak intensity ratio is a smaller value, which isoften less than 1.

By employing the synthesis conditions and synthesis procedures describedin the specification of the present application, a positive activematerial having high performance as described above can be obtained.Particularly, there can be provided a positive active material for anonaqueous electrolyte secondary battery with which a high dischargecapacity can be obtained even when the charge upper limit potential ofpositive electrode is set to lower than 4.5, e.g., a charge upper limitpotential such as 4.4 V or 4.3 V is set.

For producing a nonaqueous electrolyte secondary battery capable ofsecuring a sufficient discharge capacity even if the foregoing “positiveactive material which contains a lithium transition metal compositeoxide having an α-NaFeO₂-type crystal structure and represented by thecomposition formula: Li_(1+α)Me_(1−α)O₂ (wherein Me is a transitionmetal element including Co, Ni and Mn; and α>0), wherein the molar ratioof Li to the transition metal element Me (Li/Me) is 1.2 to 1.6”, isused, and such a charge method that the maximum ultimate potential of apositive electrode during charge is 4.3 V (vs. Li/Li⁺) or less duringuse of the battery is employed, it is preferred that a charge step(high-potential formation) taking into consideration a behaviorcharacteristic to the above-mentioned positive active material asdescribed below is provided in an initial charge-discharge step, one ofthe steps of the production process of the nonaqueous electrolytesecondary battery. That is, when constant current charge is continuedusing this active material for the positive electrode, a region where apotential change is relatively flat with respect to an amount of chargeis observed for a relatively long period of time in a positive electrodepotential range of 4.3 V to 4.8 V. FIG. 1 shows a positive electrodepotential behavior when charge is first performed to a positiveelectrode using a positive active material prepared in Example 1. Asseen in FIG. 1, a region where a potential change is relatively flat ata potential of around 4.45 V as compared to a potential of around 4.00 Vis observed for a long period of time from around the time when theamount of charge exceeds 100 mAh/g during charge in high-potentialformation.

In the charge step, a charge capacity per negative active material ispreferably 372 mAh/g or more.

The theoretical insertion capacity of Li in graphite (theoretical chargecapacity) is 372 mAh/g. Therefore, if charge exceeding the theoreticalcapacity is performed, a phenomenon of deposition of a Li metal mayoccur, leading to deterioration of life characteristics such as cycleperformance and heat stability.

On the other hand, amorphous carbon has a charge capacity of more than372 mAh/g, so that Li can be inserted without deposition of a Li metaleven in the charge described above.

Therefore, by adding amorphous carbon to graphite, the charge capacityof the negative electrode can be increased during high-potentialformation, so that the utilization factor of the negative electrode canbe considerably enhanced. Accordingly, the capacity of the battery canbe enhanced while cycle performance and the like are maintained.

These effects particularly effectively act when charge that is equal toor more than the theoretical charge capacity of graphite is performed,thus making it possible to achieve a battery having high performancethat cannot be attained by conventional graphite negative electrodes.

Example 1 Example 1-1 Preparation of Positive Active Material

Cobalt sulfate heptahydrate (14.06 g), nickel sulfate hexahydrate (20.97g) and manganese sulfate pentahydrate (65.15 g) were weighed, andtotally dissolved in 200 ml of ion exchange water to prepare a 2 Maqueous sulfate solution in which the molar ratio of Co:Ni:Mn was0.125:0.199:0.676. 750 ml of ion exchange-water was poured into a 2 dm³reaction tank, and a CO₂ gas was bubbled for 30 min to thereby dissolvethe CO₂ gas in ion exchange water. The temperature of the reaction tankwas set at 50° C. (±2° C.), and the aqueous sulfate solution was addeddropwise at a rate of 3 ml/min while the contents in the reaction tankwas stirred at a rotation speed of 700 rpm using a paddle impellerequipped with a stirring motor. The control was performed so that pH inthe reaction tank was kept at 7.9 (±0.05) by appropriately addingdropwise an aqueous solution containing 2.00 M sodium carbonate and 0.20M ammonia during dropwise addition of the aqueous sulfate solution.After completion of dropwise addition, stirring the contents in thereaction tank was continued for further 1 h. After stirring was stopped,the reaction tank was left standing for 12 h or more. By leavingstanding the reaction tank, particles of a coprecipitation carbonategenerated in the reaction tank can be sufficiently grown. Next,particles of a coprecipitation carbonate generated in the reaction tankwere separated using a suction filtration device. Sodium ions attachedon the particles were further washed off under conditions of performingwashing five times, with one-time washing including performing washingusing 200 ml of ion exchange water. The particles were dried at 80° C.for 20 hours under normal pressure in an air atmosphere using anelectric furnace. Thereafter, the particles were crushed over a fewminutes by an automatic mortar made of agate for equalizing the particlesize. In this way, a coprecipitation carbonate precursor was prepared.

For the resulting coprecipitation carbonate precursor, the color phasewas measured using Color Reader CR10 manufactured by KONICA MINOLTA, andthe results were dL=+8, da=+4 and db=+8 with respect to standard colorF05-20B of Standard Paint Colors (JPMA Standard Paint Colors)(Edition F,2011) conforming to JIS Z 8721 and issued by Japan Paint ManufacturersAssociation.

Lithium carbonate (0.970 g) was added to the coprecipitation carbonateprecursor (2.278 g), and the mixture was adequately mixed using anautomatic mortar made of agate to prepare a mixed powder of which themolar ratio of Li:(Co, Ni, Mn) was 1.30:1.00. The powder was molded at apressure of 6 MPa using a pellet molding machine to form a pellet havinga diameter of 25 mm. The amount of the mixed powder subjected to pelletmolding was determined by performing conversion calculation so that themass as an expected final product would be 2 g. One of the pellets wasplaced in an alumina boat having a total length of about 100 mm, theboat was placed in a box-type electric furnace (model: AMF 20), thetemperature was elevated from ordinary temperature to 900° C. undernormal pressure in an air atmosphere over 10 hours, and the pellet wassintered at 900° C. for 4 h. The box-type electric furnace had aninternal dimension of 10 cm (height), 20 cm (width) and 30 cm (depth),and provided with electrically heated wires at intervals of 20 cm in thewidth direction. After calcination, a heater was switched off, thealumina boat was naturally cooled as it was left standing in thefurnace. As a result, the temperature of the furnace decreased to about200° C. after 5 hours, but the subsequent temperature fall rate wasslightly low. After elapse of a whole day and night, the pellet wastaken out after confirming that the temperature of the furnace was nothigher than 100° C., and crushed by an automatic mortar made of agatefor equalizing the particle size. In this way, a lithium transitionmetal composite oxide Li_(1.13)Co_(0.11)Ni_(0.17)Mn_(0.59)O₂ containingNa (2100 ppm) according to Example 1-1 was prepared.

(Measurement of Particle Size)

For the lithium transition metal composite oxide according to Example1-1, particle size distribution measurements were made in accordancewith the following conditions and procedure. Microtrac (model: MT 3000)manufactured by Nikkiso Co., Ltd. was used as a measuring apparatus. Themeasuring apparatus includes an optical stage, a sample supply sectionand a computer including control software, and a wet cell having a laserlight transmission window is placed on the optical stage. For themeasurement principle, a wet cell, through which a dispersion with ameasurement object sample dispersed in a dispersive solvent iscirculated, is irradiated with laser light, and a distribution ofscattered light from the measurement sample is converted into a particlesize distribution. The dispersion is stored in a sample supply section,and cyclically supplied to the wet cell by a pump. The sample supplysection constantly receives ultrasonic vibrations. In this measurement,water was used as a dispersive solvent. Microtrac DHS for Win 98 (MT3000) was used as measurement control software. For “substanceinformation” set and input in the measuring apparatus, a value of 1.33was set as the “refractive index” of the solvent, “Transparent” wasselected as the “transparency”, and “Nonspherical” was selected as the“spherical particle”. A “Set Zero” operation is performed prior tomeasurement of the sample. The “Set Zero” operation is an operation forsubtracting influences on subsequent measurements of disturbance factors(glass, contamination of the glass wall face, glass irregularities,etc.) other than scattered light from particles, wherein only water as adispersive solvent is fed in a sample supply section, a backgroundoperation is performed with only water as a dispersive solvent beingcirculated through a wet cell, and background data is stored in acomputer. Subsequently, a “Sample LD (Sample Loading)” operation isperformed. The Sample LD operation is an operation for optimizing theconcentration of a sample in a dispersion that is cyclically supplied toa wet cell during measurement, wherein a measurement object sample ismanually introduced into a sample supply section in accordance withinstructions of measurement control software until an optimum amount isreached. Subsequently, a “measurement” button is depressed, so that ameasurement operation is performed. The measurement operation isrepeated twice and as an average thereof, a measurement result is outputfrom a computer. The measurement result is acquired as a particle sizedistribution histogram, and the values of D10, D50 and D90 (D10, D50 andD90 are particle sizes at which the cumulative volume in the particlesize distribution of secondary particles is 10%, 50% and 90%,respectively. Value of D50 measured was 5 μm.

(Pore Volume Distribution Measurement)

For the lithium transition metal composite oxide according to Example1-1, pore volume distribution measurements were made in accordance withthe following conditions and procedure. For measurement of the porevolume distribution, “Autosorb iQ” and control/analysis software“ASiQwin” manufactured by Quantachrome Instruments were used. A lithiumtransition metal composite oxide (1.00 g) as a sample to be measured wasplaced in a sample tube for measurement, and vacuum-dried at 120° C. for12 h to sufficiently remove moisture in the measurement sample. Next, bya nitrogen gas adsorption method using liquid nitrogen, isotherms on theadsorption side and the desorption side were measured at a relativepressure P/P0 (P0=about 770 mmHg) ranging from 0 to 1. Then, a poredistribution was evaluated by performing a calculation by BJH methodusing the isotherm on the desorption side.

In the lithium transition metal composite oxide according to Example1-1, the pore sizes, at which the differential pore volume determined byBJH method from an adsorption isotherm obtained using a nitrogen gasadsorption method shows a maximum value, were in a range of 30 to 40 nm,and the peak differential pore volume was 1.39 mm³/(g·nm).

(Configuration of Battery)

The lithium transition metal composite oxide prepared as described abovewas used as a positive active material for a nonaqueous electrolytesecondary battery to prepare a nonaqueous electrolyte secondary batteryin accordance with the following procedure.

(Positive Electrode)

A applying paste was prepared in which a positive active material,acetylene black (AB) and polyvinylidene fluoride (PVdF) were mixed at amass ratio of 90:5:5 and dispersed with N-methylpyrrolidone as adispersion medium. The applying paste was applied to one surface of analuminum foil current collector having a thickness of 20 μm and dried toprepare a positive electrode plate. The mass of the active materialapplied per unit area was 5 mg/cm². Pressing was performed using a rollpress so that the porosity of the electrode was 35%.

(Negative Electrode)

A applying paste was prepared in which an active material formed bymixing graphite and amorphous carbon at a mass ratio of 95:5 andpolyvinylidene fluoride (PVdF) were mixed at a mass ratio of 94:6 anddispersed with N-methylpyrrolidone as a dispersion medium. The applyingpaste was applied to one surface of a copper foil current collectorhaving a thickness of 20 μm and dried to prepare a negative electrodeplate.

SFG 15 manufactured by TIMCAL Ltd. was used for graphite as a negativeactive material, and CARBOTRON P (hard carbon) manufactured by KUREHACORPORATION was used for amorphous carbon.

The mass of the active material applied per unit area was 4 mg/cm².Pressing was performed using a roll press so that the porosity of theelectrode was 35%.

(Thicknesses of Positive Electrode and Negative Electrode)

In the nonaqueous electrolyte secondary batteries of Examples 1-1 to 1-7and Comparative Examples 1-1 to 1-5, the sum of electrode thickness ofthe positive electrode and the negative electrode was fixed to 92 μm.

(Assembly of Battery)

As an electrolyte solution, a solution obtained by dissolving LiPF₆, ina concentration of 1 mol/l, in a mixed solvent of ethylene carbonate(EC)/ethylmethyl carbonate (EMC)/dimethyl carbonate (DMC) in a volumeratio of 6:7:7, was used. As a separator, a microporous membrane made ofpolypropylene, the surface of which was modified with polyacrylate, wasused. Further, a bar formed by bonding a lithium metal foil to a nickelplate was placed as a reference electrode. As a sheath, a metal resincomposite film made of polyethylene terephthalate (15 μm)/aluminum foil(50 μm)/metal-adhesive polypropylene film (50 μm) was used. Theelectrode was stored such that the open ends of a positive electrodeterminal, a negative electrode terminal and a reference electrodeterminal were externally exposed. Fusion margins with the inner surfacesof the aforementioned metal resin composite films facing each other wereairtightly sealed except a portion forming an electrolyte solutionfilling hole. The electrolyte solution was injected, followed by sealingthe electrolyte solution filling hole.

(Initial Charge-Discharge Step (High-Potential Formation))

In the battery assembled in the manner described above, initial chargewas performed so that an amount of electricity per positive activematerial was 320 mAh/g while an amount of electricity per negativeactive material was 400 mAh/g. The charge was constant current chargewith a charge current of 0.1 CmA. After 10 minutes of rest, constantcurrent discharge with a discharge current of 0.1 CmA and a finalvoltage of 2.0 V was performed. The environmental temperature of initialcharge-discharge step was 25° C. The ratio of a discharge capacity to acharge capacity at this time is “initial efficiency”. In a behavior ofthe negative electrode potential monitored with respect to the referenceelectrode at the same time, a battery, in which a region where apotential change was flat (potential plateau) was not observed at around0 V (vs. Li/Li⁺) in the initial stage of discharge as shown in FIG. 2,is considered to have no electrodeposition (phenomenon of deposition oflithium metal on negative electrode) and rated “o”, and a battery, inwhich a potential plateau was observed as shown in FIG. 3, is consideredto have electrodeposition and rated “x”.

In this way, the nonaqueous electrolyte secondary battery according toExample 1-1 was prepared.

Examples 1-2 to 1-7

Nonaqueous electrolyte secondary batteries according to Examples 1-2 to1-7 were prepared in the same manner as in Example 1-1 except that themass ratio of graphite and amorphous carbon was changed from 95:5 to thevalues described in Table 1.

Comparative Example 1-1

A nonaqueous electrolyte secondary battery according to ComparativeExample 1-1 was prepared in the same manner as in Example 1-1 exceptthat a mixture of graphite and amorphous carbon was changed to graphitealone.

Comparative Example 1-2

A nonaqueous electrolyte secondary battery according to ComparativeExample 1-2 was prepared in the same manner as in Example 1-1 exceptthat a mixture of graphite and amorphous carbon was changed to graphitealone, and conditions for the above-described initial charge-dischargestep (high-potential formation) were changed to the following conditionsunder which electrodeposition (phenomenon of deposition of lithium metalon negative electrode) would not occur.

(Initial Charge-Discharge Step (High-Potential Formation))

Constant current constant voltage charge with a current of 0.1 CmA and avoltage of 4.5 V was performed. The charge termination condition was setat a time point at which the current value decreased to 0.02 CmA.Further, after 10 minutes of rest, constant current discharge with acurrent of 0.1 CmA and a final voltage of 2.0 V was performed. Theenvironmental temperature of the initial charge-discharge step was 25°C. The ratio of a discharge capacity to a charge capacity at this timeis “initial efficiency”. In a behavior of the negative electrodepotential monitored with respect to the reference electrode at the sametime, a potential plateau was not observed at around 0 V in the initialstage of discharge, and therefore the battery according to ComparativeExample 1-2 was confirmed to have no electrodeposition.

Comparative Example 1-3

A nonaqueous electrolyte secondary battery according to ComparativeExample 1-3 was prepared in the same manner as in Example 1-1 exceptthat a mixture of graphite and amorphous carbon was changed to amorphouscarbon alone.

Comparative Example 1-4

A nonaqueous electrolyte secondary battery according to ComparativeExample 1-4 was prepared in the same manner as in Example 1-1 exceptthat the mass ratio of graphite and amorphous carbon was changed from95:5 to 98:2.

Comparative Example 1-5

A nonaqueous electrolyte secondary battery according to ComparativeExample 1-5 was prepared in the same manner as in Example 1-1 exceptthat the mass ratio of graphite and amorphous carbon was changed from95:5 to 30:70.

Comparative Examples 1-6 and 1-7

A positive electrode was prepared in the same manner as in Example 1-1except that GNCM01 (manufactured by NIHON KAGAKU SANGYO CO., LTD.)having a composition of LiCo_(1/3)Ni_(1/3)Mn_(1/3)O₂ was used as apositive active material in place ofLi_(1.13)Co_(0.11)Ni_(0.17)Mn_(0.59)O₂, and a change was made so thatthe mass of an active material applied per unit area of the positiveelectrode was 8.4 mg/cm². Except that conditions for the initialcharge-discharge step were changed to the following conditions as formatters other than the positive electrode, a nonaqueous electrolytesecondary battery according to Comparative Example 1-6 was prepared inthe same manner as in Comparative Example 1-1, and a nonaqueouselectrolyte secondary battery according to Comparative Example 1-7 wasprepared in the same manner as in Example 1-2.

(Initial Charge-Discharge Step)

Initial charge was performed so that an amount of electricity perpositive active material was 155 mAh/g while an amount of electricityper negative active material was 327 mAh/g. The charge was constantcurrent charge with a charge current of 0.1 CmA. After 10 minutes ofrest, constant current discharge with a discharge current of 0.1 CmA anda final voltage of 2.0 V was performed. The environmental temperatureduring charge/discharge was 25° C. The ratio of a discharge capacity toa charge capacity at this time is “initial efficiency”. In a behavior ofthe negative electrode potential monitored with respect to the referenceelectrode at the same time, a potential plateau was not observed ataround 0 V in the initial stage of discharge, and therefore thesebatteries were confirmed to have no electrodeposition.

<Battery Test>

(Battery Capacity)

After the initial charge-discharge step, the batteries of Examples 1-1to 1-7 and Comparative Examples 1-1 to 1-7 were subjected to constantcurrent constant voltage charge with a current of 0.1 CmA and a voltageof 4.2 V after 10 minutes of rest. The charge termination condition wasset at a time point at which the current value decreased to 0.02 CmA.Further, after 10 minutes of rest, constant current discharge with acurrent of 0.1 CmA and a final voltage of 2.0 V was performed, and thedischarge capacity at this time was defined as a “battery capacity(mAh)”. The environmental temperature during charge/discharge was 25° C.

(Low SOC Power)

Further, after 10 minutes of rest, constant current constant voltagecharge with a current of 0.1 CmA and a voltage of 4.2 V was performed.The charge termination condition was set at a time point at which thecurrent value decreased to 0.02 CmA. After 10 minutes of rest, a currentwas passed in an electricity amount of 70% of the value of theaforementioned “battery capacity (mAh)”, and at this time point,discharge was stopped. Thereafter, a test of performing discharge for 1second at each rate of discharge current was conducted. Specifically,first, discharge was performed at a current of 0.1 CmA for 1 second, andafter 2 minutes of rest, auxiliary charge was performed at a current of0.1 CmA for 1 second. Further, after 2 minutes of rest, discharge wasperformed at a current of 1 CmA for 1 second, and after 2 minutes ofrest, auxiliary charge was performed at a current of 0.1 CmA for 10seconds. Further, after 2 minutes of rest, discharge was performed at acurrent of 2 CmA for 1 second, and after 2 minutes of rest, auxiliarycharge was performed at a current of 0.1 CmA for 20 seconds. From theintercept and gradient of a graph obtained by plotting a voltage 1second after each rate of discharge against a current value thereof fromthe result of the test described above, and performing fitting by aleast square method, a direct current resistance R and E0, i.e. a pseudovoltage value of a discharge current 0 CA were each calculated. A powerat SOC 30% was determined from the following formula on the assumptionthat the end-of-discharge voltage was 2.5 V. The power at this time wasrecorded as a “low SOC power (W)”.Low SOC power(W)=2.5×(E0−2.5)/R

The environmental temperature of this test was 25° C.

(Cycle Capacity Retention Ratio)

Further, after 10 minutes of rest, constant current constant voltagecharge with a current of 1 CmA and a voltage of 4.2 V was performed. Thecharge termination condition was set at a time point at which thecurrent value decreased to 0.02 CmA. After 10 minutes of rest, constantcurrent discharge with a current of 0.1 CmA and a final voltage of 2.0 Vwas performed, followed by 10 minutes of rest. These operations were allperformed under an environment at 25° C. With this series of processesas one cycle, the ratio of a discharge capacity obtained at the 15thcycle to a discharge capacity obtained at the 1st cycle was recorded asa “cycle capacity retention ratio”.

The test results for the nonaqueous electrolyte secondary batteriesaccording to Examples 1-1 to 1-7 and Comparative Examples 1-1 to 1-7 areshown in Table 1.

TABLE 1 1 CmA Low Ratio of Battery cycle SOC Positive Ratio of amorphousInitial Electro- capacity retention power electrode Negative electrodegraphite carbon efficiency deposition (mAh) ratio (W) Example 1-1Li_(1+α)Me_(1−α)O₂ Graphite/amorphous carbon 95 5 92.3% ∘ 22.4 95% 17Example 1-2 Li_(1+α)Me_(1−α)O₂ Graphite/amorphous carbon 90 10 90.7% ∘22.4 95% 20 Example 1-3 Li_(1+α)Me_(1−α)O₂ Graphite/amorphous carbon 8020 88.3% ∘ 22.2 96% 21 Example 1-4 Li_(1+α)Me_(1−α)O₂ Graphite/amorphouscarbon 70 30 87.0% ∘ 21.5 96% 22 Example 1-5 Li_(1+α)Me_(1−α)O₂Graphite/amorphous carbon 60 40 84.8% ∘ 20.7 96% 23 Example 1-6Li_(1+α)Me_(1−α)O₂ Graphite/amorphous carbon 50 50 82.5% ∘ 20.1 96% 24Example 1-7 Li_(1+α)Me_(1−α)O₂ Graphite/amorphous carbon 40 60 78.6% ∘18.9 96% 24 Comparative Li_(1+α)Me_(1−α)O₂ Graphite 100 o 93.0% x 22.565% 15 Example 1-1 Comparative Li_(1+α)Me_(1−α)O₂ Graphite 100 0 93.0% ∘18.4 95% 16 Example 1-2 Comparative Li_(1+α)Me_(1−α)O₂ Amorphous carbon0 100 65.0% ∘ 15.0 96% 26 Example 1-3 Comparative Li_(1+α)Me_(1−α)O₂Graphite/amorphous carbon 98 2 92.6% x 22.5 67% 16 Example 1-4Comparative Li_(1+α)Me_(1−α)O₂ Graphite/amorphous carbon 30 70 74.2% ∘18.1 96% 25 Example 1-5 Comparative LiMeO₂ Graphite 100 0 92.8% ∘ 17.598% 35 Example 1-6 Comparative LiMeO₂ Graphite/amorphous carbon 90 1090.7% ∘ 17.2 98% 32 Example 1-7

From Table 1, it is apparent that in the case of nonaqueous electrolytesecondary batteries of Examples 1-1 to 1-7 using in combination apositive active material containing a lithium transition metal compositeoxide represented by the composition formula: Li_(1+α)Me_(1−α)O₂(wherein Me is a transition metal element including Co, Ni and Mn; andα>0) and a negative active material which contains a carbon materialthat is a mixture of graphite and amorphous carbon and in which theratio of the amorphous carbon contained in the carbon material is 5 to60% by mass, even if high-potential formation is performed, depositionof Li does not occur on the negative electrode, the battery capacity isas large as about 19 mAh or more, and the low SOC power is improved tothe extent of 17 W or more. When the ratio of the amorphous carbon is 10to 50% by mass, the battery capacity becomes 20 mAh or more, the low SOCpower becomes 20 W or more, and initial efficiency is improved to 82.5%or more, and therefore the ratio of the amorphous carbon is preferablyin the above-mentioned range. Particularly, the ratio of the amorphouscarbon is more preferably 10 to 30% by mass because the battery capacitybecomes 21.5 mAh or more, and initial efficiency becomes 87%.

On the other hand, in the case where a negative active material in whichthe ratio of the amorphous carbon contained in a mixture of graphite andamorphous carbon is 2% by mass is used, when high-potential formation isperformed, deposition of Li occurs on the negative electrode, cycleperformance is significantly deteriorated and the low SOC power isreduced (Comparative Example 1-4). In the case where a negative activematerial in which the ratio of the amorphous carbon is 70% by mass isused, the low SOC power is improved, but the battery capacity isreduced, and initial efficiency is deteriorated (Comparative Example1-5).

Therefore, for increasing the battery capacity and improving the low SOCpower in a nonaqueous electrolyte secondary battery using a“lithium-excess-type” positive active material, it is necessary to useas a negative active material a carbon material in which the ratio ofthe amorphous carbon contained in a mixture of graphite and amorphouscarbon is 5 to 60% by mass.

In the case of a nonaqueous electrolyte secondary battery using incombination a positive active material which contains a lithiumtransition metal composite oxide represented by the composition formula:Li_(1+α)Me_(1−α)O₂ (wherein Me is a transition metal element includingCo, Ni and Mn; and α>0) and having a Li/Me ratio of 1.3 and a negativeactive material composed of graphite, when high-potential formation isperformed, deposition of Li occurs on the negative electrode, cycleperformance is significantly deteriorated, and the low SOC power isreduced (Comparative Example 1-1). When the condition in initialformation is changed to the electrodeposition of Li does not occur,deposition of Li does not occur on the negative electrode, but thebattery capacity is reduced, and the low SOC power is reduced(Comparative Example 1-2).

On the other hand, in the case of a nonaqueous electrolyte secondarybattery using in combination the aforementioned positive active materialand a negative active material composed of amorphous carbon, the low SOCpower is improved, but the battery capacity is significantly reduced,and initial efficiency is significantly deteriorated (ComparativeExample 1-3).

Nonaqueous electrolyte secondary batteries using a “lithium-excess-type”positive active material have been discussed above, and nonaqueouselectrolyte secondary batteries using a “LiMeO₂-type” positive activematerial can be as described below.

In the case of a nonaqueous electrolyte secondary battery using incombination a “LiMeO₂-type” positive active material and a negativeactive material composed of graphite, the battery capacity is small(17.5 mAh), but the low SOC power is high (35 W) as shown in ComparativeExample 1-6. Here, even if the positive active material is combined witha negative active material formed by mixing amorphous carbon withgraphite (mass ratio of graphite:amorphous carbon=90:10), there islittle change in battery capacity (17.2 mAh) and the low SOC power isnot improved (32 W) as shown in Comparative Example 1-7.

Therefore, the effect of improving a low SOC power by combination with anegative active material formed by mixing amorphous carbon with graphitecan be considered to be specific to a nonaqueous electrolyte secondarybattery using “lithium-excess-type” positive active material.

In this Example, the initial charge-discharge step includes only onecycle, but a plurality of cycles may be performed. At this time,high-potential formation may be applied for all of the plurality ofcycles, or high-potential formation may be applied for only some of theplurality of cycles. In other words, high-potential formation should beemployed for at least one cycle in the initial charge-discharge step.

It is not necessary that high-potential formation be performed at thetime of initial charge-discharge of the battery, and high-potentialformation may be performed at any time during the initialcharge-discharge step. In this case, the above-mentioned “initialefficiency” corresponds to a ratio of a discharge capacity to an amountof charge in a cycle in which high-potential formation is firstperformed (charge-discharge efficiency).

Example 2

In this Example, experiments were conducted while the ratio of amorphouscarbon contained in a mixture of graphite and amorphous carbon, i.e. anegative active material was fixed to 10% by mass or 50% by mass, andcrystallinity of amorphous carbon was changed. Crystallinity ofamorphous carbon was estimated from the half width of X-ray diffractiondata for soft carbon, soft carbon after ball-milling treatment, hardcarbon and hard carbon after ball-milling treatment, which were used inExamples shown below.

Example 2-1

A nonaqueous electrolyte secondary battery according to Example 2-1 wasprepared in the same manner as in Example 1-2 (the ratio of amorphouscarbon contained in a mixture of graphite and amorphous carbon was 10%by mass) except that as a negative active material, SFG 15 manufacturedby TIMCAL Ltd. was used for graphite and soft carbon (S001-14C3manufactured by Hitachi Chemical Company, Ltd.) was used for amorphouscarbon.

Examples 2-2 to 2-4

Soft carbon identical to that in Example 2-1 was used, and the followingmilling step (ball-milling treatment) was added. Nonaqueous electrolytesecondary batteries according to Examples 2-2 to 2-4 were prepared inthe same manner as in Example 2-1 except that a powder of soft carbonwas put beforehand in an alumina pot including 10 alumina balls having adiameter of 10 mm, the pot was set in a planetary ball mill(pulverisette 5 manufactured by FRITSCH Company), and milling wasperformed at 350 rpm for 1 hour for Example 2-2, for 2 hours for Example2-3 and for 5 hours for Example 2-4.

Example 2-5

A nonaqueous electrolyte secondary battery according to Example 2-5 wasprepared in the same manner as in Example 1-2 using hard carbonidentical to that in Example 1-2.

Comparative Examples 2-1 and 2-2

Nonaqueous electrolyte secondary batteries according to ComparativeExamples 2-1 and 2-2 were prepared in the same manner as in Example 2-5except that a powder of hard carbon was put beforehand in an alumina potincluding 10 alumina balls having a diameter of 10 mm, the pot was setin a planetary ball mill (pulverisette 5 manufactured by FRITSCHCompany), and milling was performed at 350 rpm for 2 hours forComparative Example 2-1 and for 5 hours for Comparative Example 2-2.

Example 2-6

A nonaqueous electrolyte secondary battery according to Example 2-6 wasprepared in the same manner as in Example 2-1 except that the ratio ofsoft carbon contained in a mixture of graphite and soft carbon was 50%by mass.

Examples 2-7 to 2-9

Nonaqueous electrolyte secondary batteries according to Examples 2-7 to2-9 were prepared in the same manner as in Example 2-6 except that apowder of soft carbon was put beforehand in an alumina pot including 10alumina balls having a diameter of 10 mm, the pot was set in a planetaryball mill (pulverisette 5 manufactured by FRITSCH Company), and millingwas performed at 350 rpm for 1 hour for Example 2-7, for 2 hours forExample 2-8 and for 5 hours for Example 2-9.

Example 2-10

A nonaqueous electrolyte secondary battery according to Example 2-10 wasprepared in the same manner as in Example 1-6 using hard carbonidentical to that in Example 1-6.

Comparative Examples 2-3 and 2-4

Nonaqueous electrolyte secondary batteries according to ComparativeExamples 2-3 and 2-4 were prepared in the same manner as in Example 2-10except that a powder of hard carbon was put beforehand in an alumina potincluding 10 alumina balls having a diameter of 10 mm, the pot was setin a planetary ball mill (pulverisette 5 manufactured by FRITSCHCompany), and milling was performed at 350 rpm for 2 hours forComparative Example 2-3 and for 5 hours for Comparative Example 2-4.

(Measurement of Half Width of Amorphous Carbon)

For amorphous carbon used for the negative active materials according toExamples 2-1 to 2-10 and Comparative Examples 2-1 to 2-4, the half widthwas determined by making an X-ray diffraction measurement in accordancewith the following conditions and procedure. A powder X-ray diffractionmeasurement was made using an X-ray diffractometer (manufactured byRigaku Corporation, Model: MiniFlex II). The radiation source was CuKα,and the acceleration voltage and current were 30 kV and 15 mA,respectively. For the obtained X-ray diffraction data, the half widthwas determined for the diffraction peak present at 2θ=27°±2° on an X-raydiffraction chart using “PDXL”, attached software of the X-raydiffractometer.

<Battery Test>

For the batteries of Examples 2-1 to 2-10 and Comparative Examples 2-1to 2-4, a test was conducted in the same manner as in Example 1 todetermine the battery capacity and the low SOC power. Charge/dischargewas performed under the following conditions to determine dischargeenergy.

(Discharge Energy)

After the initial charge-discharge step, the batteries of Examples 2-1to 2-10 and Comparative Examples 2-1 to 2-4 were subjected to constantcurrent constant voltage charge with a current of 0.1 CmA and a voltageof 4.2 V after 10 minutes of rest. The charge termination condition wasset at a time point at which the current value decreased to 0.02 CmA.Further, after 10 minutes of rest, constant current discharge with acurrent of 0.1 CmA and a final voltage of 2.0 V was performed, andenergy at the time of the constant current discharge was defined as“discharge energy (mWh)”. The environmental temperature duringcharge/discharge was 25° C.

The test results for the nonaqueous electrolyte secondary batteriesaccording to Examples 2-1 to 2-10 and Comparative Examples 2-1 to 2-4are shown in Table 2.

TABLE 2 Low Ratio of Half Electro- Discharge Battery SOC amorphous widthdep- energy capacity power carbon (degree) osition (mWh) (mAh) (W)Example 2-1 10 2.1 ∘ 83 23.0 22 Example 2-2 10 3.2 ∘ 81 22.7 22 Example2-3 10 4.4 ∘ 79 22.5 20 Example 2-4 10 5.1 ∘ 79 22.5 18 Example 2-5 106.0 ∘ 78 22.4 20 Comparative 10 6.7 ∘ 65 18.9 18 Example 2-1 Comparative10 7.3 ∘ 61 18.2 16 Example 2-2 Example 2-6 50 2.1 ∘ 75 22.0 22 Example2-7 50 3.2 ∘ 74 21.5 23 Example 2-8 50 4.4 ∘ 71 21.0 21 Example 2-9 505.1 ∘ 69 20.5 20 Example 2-10 50 6.0 ∘ 68 20.1 24 Comparative 50 6.7 ∘58 17.2 23 Example 2-3 Comparative 50 7.3 ∘ 53 15.7 22 Example 2-4

From Table 2, it has been apparent that when the half width of amorphouscarbon contained in a mixture of graphite and amorphous carbon is 6.0°or less, discharge energy as a battery is improved, and the batterycapacity and the low SOC power are increased.

When the half width of amorphous carbon is large and crystallinity islow, a nonaqueous electrolyte secondary battery having a high batterycapacity and a high power cannot be obtained, and therefore amorphouscarbon that is used in the nonaqueous electrolyte secondary battery ofthe present invention is preferably one having a small half width andhigh crystallinity.

Example 3

In Example 1, as a lithium transition metal composite oxide representedby the composition formula: Li_(1+α)+Me_(1−α)O₂ (wherein Me is atransition metal element including Co, Ni and Mn; and α>0), one having aLi/Me molar ratio, i.e. (1+α)/(1−α), of 1.3 was used to conductexperiments, but in this Example, those having Li/Me molar ratios of1.25 and 1.4, respectively, were used to conduct experiments.

Example 3-1

A nonaqueous electrolyte secondary battery according to Example 3-1 wasprepared in the same manner as in Example 1-2 except that 0.942 g oflithium carbonate was added to 2.304 g of the coprecipitation carbonateprecursor in stead of adding 0.970 g of lithium carbonate to 2.278 g ofthe coprecipitation carbonate precursor, the Li/Me molar ratio waschanged from 1.3 to 1.25, and a lithium transition metal composite oxideLi_(1.11)Co_(0.11)Ni_(0.18)Mn_(0.60)O₂ containing 2100 ppm of Na wasprepared.

A nonaqueous electrolyte secondary battery according to Example 3-2 wasprepared in the same manner as in Example 1-2 except that 1.021 g oflithium carbonate was added to 2.228 g of the coprecipitation carbonateprecursor in stead of adding 0.970 g of lithium carbonate to 2.278 g ofthe coprecipitation carbonate precursor, the Li/Me molar ratio waschanged from 1.3 to 1.4, and a lithium transition metal composite oxideLi_(1.17)Co_(0.10)Ni_(0.17)Mn_(0.56)O₂ containing 2100 ppm of Na wasprepared.

A battery test was conducted in the same manner as in Example 1-2.

The test results for the nonaqueous electrolyte secondary batteriesaccording to Examples 3-1 and 3-2 are shown in Table 3.

TABLE 3 Ratio of Battery Li/Me Negative amorphous Electrode- capacityratio electrode carbon position (mAh) Example 1.25 Graphite/amor- 10 ◯20.5 3-1 phous carbon Example 1.4 Graphite/amor- 10 ◯ 22.5 3-2 phouscarbon

From Table 3, it is apparent that in the case of the nonaqueouselectrolyte secondary batteries of Examples 3-1 and 3-2, even ifhigh-potential formation is performed, deposition of Li does not occuron the negative electrode, and the battery capacity is as large as 20mAh or more. In the present invention, as described in paragraph [0050],amorphous carbon is mixed with graphite to form a negative activematerial, whereby a low SOC region having a high resistance, which is aweak point of the “lithium-excess-type” positive active material, can becut, so that the low SOC power is improved. Accordingly, it isconsidered that the Li/Me ratio has little influence on the low SOCpower of the battery, and therefore it can understand that the low SOCpower of the nonaqueous electrolyte secondary battery of each ofExamples 3-1 and 3-2 is comparable to that in Example 1-2, i.e. 17 W ormore.

As described above, in the present invention, a positive electrodehaving a positive active material containing a lithium transition metalcomposite oxide represented by the composition formula:Li_(1+α)Me_(1−α)O₂ (wherein Me is a transition metal element includingCo, Ni and Mn; and α>0) and a negative electrode having a negativeactive material which contains a carbon material that is a mixture ofgraphite and amorphous carbon and in which the ratio of the amorphouscarbon contained in the carbon material is 5 to 60% by mass are combinedto obtain a nonaqueous electrolyte secondary battery having a largebattery capacity and a high power while deposition of Li inhigh-potential formation is suppressed.

According to the present invention, a nonaqueous electrolyte secondarybattery is obtained which has a large battery capacity and a high powerwhile deposition of Li on a negative electrode during high-potentialformation is suppressed, and this nonaqueous electrolyte secondarybattery is useful as a nonaqueous electrolyte secondary battery for ahybrid vehicle and an electric vehicle.

What is claimed is:
 1. A nonaqueous electrolyte secondary batterycomprising a positive electrode, a negative electrode and a nonaqueouselectrolyte, wherein the positive electrode has a positive activematerial containing a lithium transition metal composite oxide having anα-NaFeO₂-type crystal structure and represented by the compositionformula: Li_(1+α)Me_(1−α)O₂ (wherein Me is a transition metal elementincluding Co, Ni and Mn; and α>0), a ratio of moles of Mn to moles of Mebeing from 0.63 to 0.72, the lithium transition metal composite oxidecomprising 900 ppm or more and 16,000 ppm or less of Na, and thenegative electrode has a negative active material containing a carbonmaterial that is a mixture of graphite and amorphous carbon, the ratioof the amorphous carbon contained in the carbon material is 5 to 60% bymass, and a charge capacity per negative active material is 372 mAh/g ormore.
 2. The nonaqueous electrolyte secondary battery according to claim1, wherein the amorphous carbon has a half width of 6.0° or less, thehalf width being that of the (002) diffraction line in X-ray diffractionmeasurement.
 3. The nonaqueous electrolyte secondary battery accordingto claim 1, wherein the lithium transition metal composite oxidecontains 2,000 ppm or more and 10,000 ppm or less of Na.
 4. A method forproduction of a nonaqueous electrolyte secondary battery comprising apositive electrode, a negative electrode and a nonaqueous electrolyte,wherein the positive electrode has a positive active material containinga lithium transition metal composite oxide having an α-NaFeO₂-typecrystal structure and represented by the composition formula:Li_(1+α)Me_(1−α)O₂ (wherein Me is a transition metal element includingCo, Ni and Mn; and α>0), a ratio of moles of Mn to moles of Me beingfrom 0.63 to 0.72, the lithium transition metal composite oxidecomprising 900 ppm or more and 16,000 ppm or less of Na, the negativeelectrode has a negative active material containing a carbon materialthat is a mixture of graphite and amorphous carbon, and the ratio of theamorphous carbon contained in the carbon material is 5 to 60% by mass,and the method comprises a charge step in an initial charge-dischargestep in which a charge capacity per negative active material is 372mAh/g or more in the charge step.
 5. The method for production of anonaqueous electrolyte secondary battery according to claim 4 furthercomprising: providing a carbonate precursor, combining the carbonateprecursor with Na, drying the combination of the carbonate precursor andNa at a temperature of 80° C. or more and less than 100° C., sinteringthe dried combination of the carbonate precursor and Na at a temperatureof 700° C. to 950° C. to make the lithium transition metal compositeoxide.
 6. The method for production of a nonaqueous electrolytesecondary battery according to claim 4 further comprising: providing acarbonate precursor, combining the carbonate precursor with sodiumcarbonate, drying the combination of the carbonate precursor with sodiumcarbonate at a temperature of 80° C. or more and less than 100° C.,sintering the dried combination of the carbonate precursor with sodiumcarbonate at a temperature of 700° C. to 950° C. to make the lithiumtransition metal composite oxide.
 7. The nonaqueous electrolytesecondary battery according to claim 1, wherein the ratio of theamorphous carbon contained in the carbon material is 10 to 50% by mass.8. The nonaqueous electrolyte secondary battery according to claim 1,wherein the lithium transition metal composite oxide has a crystalstructure of P3₁12 or R3-m having a half width of diffraction peak at2θ=18.6°±1° of 0.20° to 0.27° or/and a half width of diffraction peak at2θ=44.1°±1° of 0.26° to 0.39°.
 9. A nonaqueous electrolyte secondarybattery comprising a positive electrode, a negative electrode and anonaqueous electrolyte, wherein the positive electrode has a positiveactive material containing a lithium transition metal composite oxidehaving an α-NaFeO₂-type crystal structure and represented by thecomposition formula: Li_(1+α)Me_(1−α)O₂ (wherein Me is a transitionmetal element including Co, Ni and Mn; and α>0), the lithium transitionmetal composite oxide having a peak differential pore volume of 0.85 to1.76 mm³/(g·nm) in a pore region of 30 to 50 nm, and the negativeelectrode has a negative active material containing a carbon materialthat is a mixture of graphite and amorphous carbon, the ratio of theamorphous carbon contained in the carbon material is 5 to 60% by mass,and a charge capacity per negative active material is 372 mAh/g or more.10. The nonaqueous electrolyte secondary battery according to claim 9,wherein a ratio of moles of Mn to moles of Me of the lithium transitionmetal composite oxide is from 0.63 to 0.72.
 11. A method for productionof the nonaqueous electrolyte secondary battery comprising a positiveelectrode, a negative electrode and a nonaqueous electrolyte, whereinthe positive electrode has a positive active material containing alithium transition metal composite oxide having an α-NaFeO₂-type crystalstructure and represented by the composition formula: Li_(1+α)Me_(1−α)O₂(wherein Me is a transition metal element including Co, Ni and Mn; andα>0), the lithium transition metal composite oxide having a peakdifferential pore volume of 0.85 to 1.76 mm³/(g·nm) in a pore region of30 to 50 nm, the negative electrode has a negative active materialcontaining a carbon material that is a mixture of graphite and amorphouscarbon, and the ratio of the amorphous carbon contained in the carbonmaterial is 5 to 60% by mass, and the method comprises a charge step inan initial charge-discharge step in which a charge capacity per negativeactive material is 372 mAh/g or more in the charge step.
 12. Anonaqueous electrolyte secondary battery comprising a positiveelectrode, a negative electrode and a nonaqueous electrolyte, whereinthe positive electrode has a positive active material containing alithium transition metal composite oxide having an α-NaFeO₂-type crystalstructure and represented by the composition formula: Li_(1+α)Me_(1−α)O₂(wherein Me is a transition metal element including Co, Ni and Mn; andα>0), the negative electrode has a negative active material containing acarbon material that is a mixture of graphite and amorphous carbon, saidamorphous carbon consists of hard carbon or soft carbon, and a chargecapacity per negative active material is 372 mAh/g or more.
 13. Thenonaqueous electrolyte secondary battery according to claim 12, whereinthe negative active material consists essentially of the carbon materialthat is the mixture of graphite and amorphous carbon.
 14. The nonaqueouselectrolyte secondary battery according to claim 12, wherein the lithiumtransition metal composite oxide comprises 900 ppm or more and 16,000ppm or less of Na.
 15. The nonaqueous electrolyte secondary batteryaccording to claim 12, wherein the ratio of the amorphous carboncontained in the carbon material is 5% by mass or more.
 16. Thenonaqueous electrolyte secondary battery according to claim 12, whereinthe ratio of the amorphous carbon contained in the carbon material is 5%by mass or more and 60% by mass or less.